MATERIAL DESCRIPTION |
PHYSCIAL PROPERTIES |
TENSILE STRENGTH Kg/mm2 |
ELONGATION % ON 5.65 OA |
FREE CUTTING BRASS TYPE I |
ANNEALED : 35 to 29
HALF HARD : 41 to 33
HARD : 56 to 50 |
ANNEALED : 12 to 22
HALF HARD : 41 to 17
HARD : - Upto 4 |
FREE CUTTING BRASS TYPE II |
ANNEALED : 34 to 28
HALF HARD : 40 to 32
HARD : 56 to 49 |
ANNEALED : 15 to 25
HALF HARD : 7 to 20
HARD : - Upto 4 |
FREE CUTTING BRASS TYPE III |
ANNEALED : 30 to 25
HALF HARD : 36 to 26
HARD : 45 to 40 |
ANNEALED : 22 to 32
HALF HARD : 8 to 27
HARD : - Upto 4 |
FORGING BRASS |
35 Min. |
25% Min. |
MODIFIED FORGING BRASS |
42.5 Min. |
25% Min. |
FORGING BRASS WITH LOW Mn |
42.0 Min. |
25% Min. |
RIVETING BRASS RODS LEAD FREE |
34.5 Min. |
25% Min. |
ANNEALED : 30 Min
HALF HARD : 47 to 63
HARD : 63 to 79 |
35% Min. |
RIVETING BRASS RODS LEADED |
OUTR HARD : 33 to 39
HALF HARD : 40 to 49
HARD : 50 to 69
E HARD : 70 to 90 |
30%
20%
15%
5% |
OUTR HARD : 33 to 39
HALF HARD : 42 to 51 |
30%
15% |
HIGH TENSILE BRASS RODS |
AS MFGD : 47
HARD : 55 |
18% 12% |
47 Min. |
20% Min. |
NAVAL BRASS ROD GRADE I |
35 to 40 |
18% Min. |
NAVAL BRASS ROD GRADE II |
40 Min. |
15% Min. |
LEADED BRASS FOR SECTIONS |
40 Min. |
15% Min. |
NICKEL SILVER ALLOY RODS |
47 Min. |
8% Min. |
COPPER ROD FOR GENERAL ENGG PURPOSE |
41 Min. |
15% Min. |